Yleispigmentit, As Powder
Main Page > Värituotteet > Yleispigmentit, As Powder
Firing range 920 - 1400°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
5,59 €
Firing range 920 - 1300°C. Chemical composition Zr-Si-V-Pr-Co-Ni-Cr-Fe.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
6,52 €
Firing range 920 - 1350°C. Chemical composition Cr-Co-Si.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
5,29 €
Firing range 920 - 1350°C. Chemical composition Cr.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
4,96 €
Firing range 920 - 1350°C. Chemical composition Cr-Co-Al-Zn.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
11,03 €
Firing range 920 - 1350°C. Chemical composition Co-Al-Cr.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
15,72 €
Firing range 920 - 1300°C. Chemical composition Cr-Co-Pr-Zr-Si-Zn.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
8,69 €
Firing range 920 - 1250ºC. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose...
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose...
from
9,47 €
Firing range 920 - 1250°C. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose...
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose...
from
9,80 €
Firing range 920 - 1300°C.
Very Black! K8553=55/3
Chemical composition Cr-Co-Fe-Ni...
Very Black! K8553=55/3
Chemical composition Cr-Co-Fe-Ni...
from
18,32 €
Firing range 920 - 1300°C. Strong colour former. K2464=46/4
Chemical composition Cr-Fe-Ni-Mn. Optimal amount when added to...
Chemical composition Cr-Fe-Ni-Mn. Optimal amount when added to...
from
8,20 €
Firing range 920 - 1300°C. Chemical composition Cr-Co-Fe-Ni-Mn
Blue-black tone.
Blue-black tone.
from
11,58 €
Polttolämpötila 920-1300°C. Lasitteeseen lisättynä optimaalinen määrä n.5-8%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
from
14,93 €
Polttolämpötila 920-1300°C. Lasitteeseen lisättynä optimaalinen määrä n.5-8%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
from
13,26 €
Firing range 920 - 1240°C. K2278=27/8
Chemical composition Sn-Ca-Si-Cr. Vaaleammassa munassa 8% pigmenttiä on lisätty transparenttiin mattalasitteeseen ja...
Chemical composition Sn-Ca-Si-Cr. Vaaleammassa munassa 8% pigmenttiä on lisätty transparenttiin mattalasitteeseen ja...
from
8,33 €
Firing range 920 - 1300°C. Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen...
from
5,46 €