Yleispigmentit, As Powder
Main Page > Värituotteet > Yleispigmentit, As Powder
4402 lila
More details
from
10,37 €
K208 Kuninkaansininen 100g
Co-Si
920º-1250ºC
Hyvin tumma koboltinsininen pigmentti.
920º-1250ºC
Hyvin tumma koboltinsininen pigmentti.
23,18 €
/100 pc
FIX69046964 Pink
Vasemmanpuoleisessa palassa kirkkaaseen läpinäkyvään lasitteeseen PR5460f:ään on sekoitettu pigmenttiä ja poltettu 1050°C. Savi E. Oikeanpuoleisessa palassa kirkkaaseen läpinäkyvään lasitteeseen PR5460f:ään on sekoitettu 10% pigmenttiä ja poltettu 1250°C. Savi GS209 Tämä pinkki kestää hyvin...
from
11,34 €
FK648 Violet
Max. temperature 1250ºC. Chemical composition Sn-Cr.
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
from
15,94 €
FK 3022 Deep Red
Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen.
Niiden sisältämä kadmium ja...
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen.
Niiden sisältämä kadmium ja...
from
14,54 €
FK6904 Red
Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen. Niiden sisältämä kadmium ja seleeni on sidottu...
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen. Niiden sisältämä kadmium ja seleeni on sidottu...
from
11,46 €
FK150 Neutral Grey
Firing range 920 - 1350°C. Chemical composition Al-Co-Ni-Zn.
Optimal amount when added to glaze approx. 5%.
Optimal amount when added to glaze approx. 5%.
from
5,16 €
FK245 Turquoise
Firing range 920 - 1350°C. Chemical composition Zr-V-Si.
Optimal amount when added to glaze approx. 4 - 6%.
Optimal amount when added to glaze approx. 4 - 6%.
from
5,57 €
FK206 Cobalt Blue
Firing range 920 - 1400°C. Chemical composition Co-Si.
Lasitteeseen lisättynä optimaalinen määrä n. 3%.
Lasitteeseen lisättynä optimaalinen määrä n. 3%.
from
13,75 €
Pi20 Karambola
Polttolämpötila 1000 - 1260°C. Pigmenttiä on varastossa reilusti, mutta rajoitettu erä. Kirkkaan keltainen pigmentti lasitteisiin ja massoihin.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F...
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F...
from
5,26 €
Pi21 Mandarin
Firing range 1000 - 1400°C. Pigmenttiä on varastossa reilusti, mutta rajoitettu erä. Oranssinkeltainen pigmentti lasitteisiin ja massoihin.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen.
Pala...
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen.
Pala...
from
9,01 €
Pi22 Kumkvatti
Polttolämpötila 1000-1300°C Pigmenttiä on varastossa reilu, mutta rajoitettu erä. Oranssinkeltainen pigmentti lasitteisiin ja massoihin.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
from
9,01 €
Pi23 Dark Cocoa
Firing range 1000 - 1300°C. Pigmenttiä on varastossa reilusti, mutta rajoitettu erä. Tummanruskea pigmentti lasitteisiin ja massoihin.
Kuvassa 4% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Piece fired at 1250°C.
Kuvassa 4% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Piece fired at 1250°C.
from
5,26 €
Pi24 Mint
Polttolämpötila 1000-1300°C Pigmenttiä on varastossa reilu, mutta rajoitettu erä. Mintunvihreä pigmentti lasitteisiin ja massoihin.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
from
5,26 €
Pi25 Coral
Firing range 1000 - 1300°C. Pigmenttiä on varastossa reilu, mutta rajoitettu erä. Korallin sävyinen pigmentti lasitteisiin ja massoihin.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
Kuvassa 10% pigmenttiä sekoitettu laajapolttoväliseen värittömään pr5460F lasitteeseen. Pala poltettu 1250°C.
from
4,96 €
FK407 Yellow
Firing range 920 - 1300°C. Chemical composition Zr-Si-Pr.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
6,28 €
FK5001 Orange
Firing range 920 - 1300°C. Chemical composition Zr-Si-Cd-S-Se.
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen.
Niiden sisältämä kadmium ja...
Optimal amount when added to glaze approx. 8 - 10%. Tähdellä merkityt pigmentit eivät sovellu kuulamyllytykseen.
Niiden sisältämä kadmium ja...
from
12,90 €
FK560 Light Green
Firing range 920 - 1250°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
9,03 €
FK4826 Mint Green
Firing range 920 - 1400°C. Chemical composition Zr-Si-Pr-V.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
5,59 €
FK 4198 Victorian Green
Firing range 920 - 1300°C. Chemical composition Zr-Si-V-Pr-Co-Ni-Cr-Fe.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
6,52 €
FK 520 Green
Firing range 920 - 1350°C. Chemical composition Cr-Co-Si.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
5,29 €
FK522 krominvihreä
Firing range 920 - 1350°C. Chemical composition Cr.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
4,96 €
FK523 Blue-Green
Firing range 920 - 1350°C. Chemical composition Cr-Co-Al-Zn.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
11,03 €
FK 546 petrooli
Firing range 920 - 1350°C. Chemical composition Co-Al-Cr.
Optimal amount when added to glaze approx. 6%.
Optimal amount when added to glaze approx. 6%.
from
15,72 €
FK 9959 Dark Green
Firing range 920 - 1300°C. Chemical composition Cr-Co-Pr-Zr-Si-Zn.
Optimal amount when added to glaze approx. 3 - 6%.
Optimal amount when added to glaze approx. 3 - 6%.
from
8,69 €
FK602a Pink
Firing range 920 - 1250ºC. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
from
9,47 €
FK604a Pink
Firing range 920 - 1250°C. Chemical composition Cr-Sn-Ca-Si
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
Optimal amount when added to glaze approx. 10%. On some glazes the pigment may lose its colour when fired over 1200°C.
from
9,80 €
K2890 Deep Grey
Firing range 920 - 1300°C. Chemical composition Fe-Cr-Co-Ni.
from
5,24 €
K4816 Neutral Grey
Firing range 920 - 1300°C. Chemical composition Fe-Cr-Co-Ni.
from
5,21 €
K8553 Black
Firing range 920 - 1300°C.
Very Black! K8553=55/3
Chemical composition Cr-Co-Fe-Ni...
Very Black! K8553=55/3
Chemical composition Cr-Co-Fe-Ni...
from
18,32 €
K2464 Black
Firing range 920 - 1300°C. Strong colour former. K2464=46/4
Chemical composition Cr-Fe-Ni-Mn. Optimal amount when added to glaze approx. 5%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
Chemical composition Cr-Fe-Ni-Mn. Optimal amount when added to glaze approx. 5%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja...
from
8,20 €
K2482 Deep Black
Firing range 920 - 1300°C. Chemical composition Cr-Co-Fe-Ni-Mn
Blue-black tone.
Blue-black tone.
from
11,58 €
51/1 Deep Red
Polttolämpötila 920-1300°C. Lasitteeseen lisättynä optimaalinen määrä n.5-8%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
14,93 €
51/2 Orange-Red
Polttolämpötila 920-1300°C. Lasitteeseen lisättynä optimaalinen määrä n.5-8%.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
13,26 €
K2278 Cherry
Firing range 920 - 1240°C. K2278=27/8
Chemical composition Sn-Ca-Si-Cr. Vaaleammassa munassa 8% pigmenttiä on lisätty transparenttiin mattalasitteeseen ja voimakkaamman värisessä kirkkaaseen kiiltävään lasitteeseen.
Chemical composition Sn-Ca-Si-Cr. Vaaleammassa munassa 8% pigmenttiä on lisätty transparenttiin mattalasitteeseen ja voimakkaamman värisessä kirkkaaseen kiiltävään lasitteeseen.
from
8,33 €
51/5 Light Blue
Firing range 920 - 1300°C. Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
5,46 €
K2317 Azure Blue
Firing range 920 - 1300°C. K2317=31/7
Chemical composition Zr-Si-V
Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen...
Chemical composition Zr-Si-V
Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen...
from
6,52 €
52/3 Royal Blue
More details
from
7,70 €
52/9 Midblue
More details
from
8,75 €
60/3 Light blue
More details
from
10,74 €
K84 Cobalt Blue
Firing range 920 - 1300°C. K84=84
Chemical composition Zr-Si-Pr.
Optimal amount when added to glaze approx. 5 - 8%.
Chemical composition Zr-Si-Pr.
Optimal amount when added to glaze approx. 5 - 8%.
from
16,82 €
K4628 Cobalt Blue
Firing range 920 - 1300°C. Chemical composition Co-Si.
Upper piece fired at 1035°C and lower at 1255°C.
Molemmissa lasitepohjana on kirkas laajapolttoinen PR5460f lasite ja pigmenttiä lisätty 3%.
Upper piece fired at 1035°C and lower at 1255°C.
Molemmissa lasitepohjana on kirkas laajapolttoinen PR5460f lasite ja pigmenttiä lisätty 3%.
from
10,82 €
29/3 Green
Firing range 920 - 1300°C.
from
12,49 €
45/1 Light Green
Firing range 920 - 1300°C. Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
13,17 €
52/1 Light Green
More details
from
16,49 €
52/2 Olive-Green
More details
from
14,92 €
K2297 Bottle Green
Firing range 920 - 1300°C. K2297=29/7
Chemical composition Cr-Co.
Optimal amount when added to glaze approx. 5%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna...
Chemical composition Cr-Co.
Optimal amount when added to glaze approx. 5%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna...
from
13,74 €
52/4 Orange-Brown
More details
from
4,12 €
53/2 Tree Brown
Polttolämpötila 920 - 1300°C. Lasitteeseen lisättynä optimaalinen määrä n. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
5,67 €
53/3 Red-Brown
Polttolämpötila 920-1300°C. Lasitteeseen lisättynä optimaalinen määrä n.5-8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
12,50 €
K2291= K2709 Brown
Code K2291 has been replaced with K2709. Firing range 920 - 1300°C. Upper piece fired at 1255°C and lower at 1050°C.
Molemmissa lasitepohjana on kirkas laajapolttoinen 921 lasite ja pigmenttiä lisätty 8%.
Molemmissa lasitepohjana on kirkas laajapolttoinen 921 lasite ja pigmenttiä lisätty 8%.
from
5,77 €
K2269 Grey
Firing range 920 - 1300°C. K2269=26/9
Chemical composition Sn-Sb.
Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen...
Chemical composition Sn-Sb.
Optimal amount when added to glaze approx. 5 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen...
from
16,87 €
K2323 Indian Yellow
Firing range 920 - 1300°C. K2323=32/3
Chemical composition Zr-V
Optimal amount when added to glaze approx. 5 - 8%.
Chemical composition Zr-V
Optimal amount when added to glaze approx. 5 - 8%.
from
14,57 €
51/4 Sunny Yellow
Firing range 920 - 1300°C.
Optimal amount when added to glaze approx. 6 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
Optimal amount when added to glaze approx. 6 - 8%. Kuvassa vaaleampi muna on lasitettu värittömällä mattalasitteella ja voimakkaamman värinen muna värittömällä kiiltävällä lasitteella, molempiin on lisätty 8% pigmenttiä.
from
11,18 €